Sanitary fittings polypropylene raw material optimization formula -

100 kg general injection grade homopolypropylene, 2 kg Zeng Gang toughening brightening masterbatch HB2005, direct mixing molding, you can greatly enhance the overall quality of sanitary ware products and injection molding production efficiency.

Good gloss, beautiful appearance

○ good hardness, impact resistance;

○ shrink uniform, small deformation;

○ high yield, high quality.

HB2005 features introduced:

● For molding of PP wall thickness molding products for a long time, can shorten the cooling setting time 50% -100%, shorten the molding cycle of 20% to 30%, a substantial increase in production efficiency;

● improve heat-resistant temperature 20 ~ 25 ℃;

● improve the rigidity of the product 30%;

● improve the surface hardness;

● improve material impact strength;

● enhance the surface gloss products;

● PP products forming cooling to achieve isometric contraction, eliminate warping deformation, to solve the contraction after deformation;

● improve product quality, reduce the production of non-performing products, to provide products with excellent dimensional stability;

● high safety, in line with ROHS certification, REACH certification, FDA certification, GB9685 list, LFGB certification, plasticizer certification;

Physical parameters

Appearance: Transparent particles Specific Gravity: 0.93g / cm3 Melt Index: 30g / cm3

Process conditions

● In the process of injection molding, PP products that increase production efficiency and shorten the cooling setting time should be adjusted according to the following process:

● The best injection temperature range of 200 ~ 220 ℃, the specific temperature according to customer's own equipment to determine the condition;

● injection pressure and injection speed according to product quality requirements and process to determine;

● Because HB2005 will make the plastic mouth quicken harden, so the packing time is shortened as far as possible without any shrinkage;

● melt time to ensure good dispersion under the premise of minimizing;

● After the end of the melt cooling setting time can be significantly shortened.